304L Nerjaveèi asye san pwoblèm konpozisyon tib
304L Nerjaveèi asye mawonnen tib
| Klas | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 | min. | – | – | – | – | – | 18.0 | – | 8.0 | – |
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||
| 304L | min. | – | – | – | – | – | 18.0 | – | 8.00 | – |
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.00 | 0.10 | ||
304L Nerjaveèi asye mawonnen tib
UNS S30403 Tib san pwoblèm pwopriyete mekanik
| Klas | Fòs rupture (MPa) min | Sede Fòs 0.2% Prèv (MPa) min | Elongasyon (% nan 50mm) min | Dite | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 | 515 | 205 | 40 | 92 | 201 |
| 304L | 485 | 170 | 40 | 92 | 201 |
304L Nerjaveèi asye mawonnen tib
Klas ekivalan pou Tib Nerjaveèi 304
| Klas | UNS No | Old Britanik | Euronorm | Swedish SS | Japonè JIS | GOST | ||
| BS | En | No | Non | |||||
| 304 | S30400 | 304S31 | 58E | 1.4301 | X5CrNi18-10 | 2332 | SUS 304 | 08Х18Н10 |
| 304L | S30403 | 304S31 | 58E | 1.4306 / 1.4307 | X5CrNi18-10 | 2332 | SUS 304L | 03Х18Н11 |