ASTM A269 310S Nerjaveèi asye bobin tib pwopriyete mekanik
Pwopriyete mekanik ASTM A269 310S asye pur tib bobin yo jan sa a: Fòs rupture: 485 MPa (70,000 psi) ak fòs sede: 215 MPa (31,000 psi)
| Klas | 310S |
| Fòs rupture (MPa) min | 515 |
| Sede Fòs 0.2% Prèv (MPa) min | 205 |
| Elongasyon (% nan 50mm) min | 40 |
| Dite | – |
| Rockwell B (HR B) max | 95 |
| Brinell (HB) max | 217 |
Konpozisyon chimik ASTM A269 310S Nerjaveèi asye bobin tib
Konpozisyon chimik ASTM A269 310S tib bobin asye pur se: Kabòn (C) - 0.08% max, Manganèz (Mn) - 2% max, Silisyòm (Si) - 1% max.
| SS | 310S |
| Ni | 10-14 |
| N | 0.10 max |
| Cr | 16-18 |
| C | 0.08 max |
| Si | 0.75 max |
| Mn | 2 max |
| P | 0.045 max |
| S | 0.030 max |
| Mo | 2.00 - 3.00 |