Entwodiksyon
Nerjaveèi yo konnen kòm asye wo-alyaj.Yo konpoze de 4-30% nan chromium.Yo klase nan martensitic, austenitic, ak ferritic asye ki baze sou estrikti cristalline yo.
Klas 317 asye pur se yon vèsyon modifye nan 316 asye pur.Li gen gwo fòs ak rezistans korozyon.Fich done sa a bay plis detay sou klas 317 asye pur.
317 mawonnen tib kapilè tib
Konpozisyon chimik
Konpozisyon chimik klas 317 asye pur endike nan tablo ki anba la a.
| Eleman | Kontni (%) |
|---|---|
| Iron, Fe | 61 |
| Kwòm, Kr | 19 |
| Nikèl, Ni | 13 |
| Molybdène, Mo | 3.50 |
| Manganèz, Mn | 2 |
| Silisyòm, Si | 1 |
| Kabòn, C | 0.080 |
| Fosfò, P | 0.045 |
| Souf, S | 0.030 |
Pwopriyete Fizik
317 mawonnen tib kapilè tib
Tablo ki anba la a montre pwopriyete fizik klas 317 asye pur.
| Pwopriyete | Metrik | Imperial |
|---|---|---|
| Dansite | 8 g/cm3 | 0.289 lb/pous³ |
| Pwen k ap fonn | 1370 °C | 2550°F |
Pwopriyete mekanik
317 mawonnen tib kapilè tib
Pwopriyete mekanik rkwit 317 asye pur yo parèt nan tablo ki anba la a.
| Pwopriyete | Metrik | Imperial |
|---|---|---|
| Fòs rupture | 620 MPa | 89900 psi |
| Sede fòs | 275 MPa | 39900 psi |
| Modil elastik | 193 GPa | 27993 ksi |
| Rapò Poisson a | 0.27-0.30 | 0.27-0.30 |
| Elongasyon nan kraze (nan 50 mm) | 45% | 45% |
| Dite, Rockwell B | 85 | 85 |
Pwopriyete tèmik
Pwopriyete tèmik klas 317 asye pur yo bay nan tablo ki anba la a.
| Pwopriyete | Metrik | Imperial |
|---|---|---|
| Koefisyan ekspansyon tèmik (@ 0-100°C/32-212°F) | 16 µm/m°C | 8.89 µin/in°F |
| Konduktivite tèmik (@ 100°C/212°F) | 16.3 W/mK | 113 BTU pous/hr.ft².°F |
Lòt Deziyasyon
Lòt deziyasyon ki ekivalan a asye pur klas 317 yo enkli nan tablo ki anba la a.
| ASTM A167 | ASTM A276 | ASTM A478 | ASTM A814 | ASME SA403 |
| ASTM A182 | ASTM A312 | ASTM A511 | QQ S763 | ASME SA409 |
| ASTM A213 | ASTM A314 | ASTM A554 | DIN 1.4449 | MIL-S-862 |
| ASTM A240 | ASTM A403 | ASTM A580 | ASME SA240 | SAE 30317 |
| ASTM A249 | ASTM A409 | ASTM A632 | ASME SA249 | SAE J405 (30317) |
| ASTM A269 | ASTM A473 | ASTM A813 | ASME SA312 |
Lè poste: Apr-14-2023